ASTM A Standard Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip. ASTM A ASME SA ASTM A ASME SA Bolts. Bars, Wire and Shapes. Sheet, Plate and Strip. Forgings. Element. Typical Composition (Weight . ASTM A – 16 Standard Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip. This guide.
|Published (Last):||26 December 2004|
|PDF File Size:||15.55 Mb|
|ePub File Size:||7.83 Mb|
|Price:||Free* [*Free Regsitration Required]|
They are suitable for machining in the solution-annealed condition, after which they may be hardened to the mechanical properties specified in this standard without danger of cracking or distortion. The steel shall conform to the required asstm properties such as tensile strength, yield strength, elongation, and hardness. This guide covers standard specification for precipitation-hardening stainless steel plate, sheet, and strip. The mechanical properties of these steels are developed by suitable low-temperature heat treatments generally referred to as precipitation hardening.
This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application.
Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.
ASTM A693 Specification
Link to Active This link will always route to the current Active version of the standard. Some of these steels are particularly suitable for moderate to severe drawing and forming in the solution-treated condition. ICS Number Code ASTM does not give any warranty express or implied or make any representation that sstm contents of this abstract are accurate, complete or up to date. Samples cut from the solution-annealed plate, sheet, or strip shall conform to the specified mechanical properties when precipitation hardened.
ASTM A Specification | Penn Stainless Products
Samples cut from the solution-annealed plate, sheet, or strip shall withstand cold bending without cracking on the outside of the bent portion. Others are capable of mild forming only.
The mechanical properties of these steels shall be developed by suitable low-temperature heat treatments or precipitation hardening. Historical Version s – view previous versions of q693. The steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, aluminum, molybdenum, titanium, copper, and other elements.